Title: Magnetic Studies on CoFe2O4Thin Films Prepared by Spin Coating Method
Authors: Rani, Neeru
Supervisor: Sharma, Puneet
Keywords: Spinel Ferrite;Thin Film;Magnetic Properties
Issue Date: 30-Aug-2017
Abstract: Cobalt ferrite thin films were prepared by sol gel spin coating method. The effect of annealing temperature and film thickness on structural and magnetic properties was investigated. The chosen annealing temperature were 700 °C, 800 °C, 900 °C, 1000 °C and film thickness were varied from 0.40 μm to 0.70μm. As the annealing temperature increased the coercivity decreased. Saturation magnetization increased with increasing annealing temperature. At 1000 °C film showed relatively high saturation magnetization (284.5emu/cc) and low coercivity (293.5Oe). The magnetic hysteresis loops for perpendicular and parallel to the planes of substrate are same. The surface morphology investigated by field emission scanning electron microscope for films fabricated at different temperature and different thickness.
Description: Master of Science -Physics
URI: http://hdl.handle.net/10266/4783
Appears in Collections:Masters Theses@SPMS

Files in This Item:
File Description SizeFormat 
4783.pdf1.23 MBAdobe PDFThumbnail
View/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.