Title: Synthesis of Nano Sized Yttria Stabilized Zirconia Powder for Thermal Barrier Coating Application
Authors: Singh, Rajpal
Supervisor: Singh, Kulvir
Keywords: Thermal Barrier Coating
Issue Date: 27-Oct-2010
Abstract: NanocrystallineYSZ p owd e r wa s p r e p a r e d b y a s imp l e c o n s ump t i o n me t h o d z i r c o n i um ox chloride octahydrate Zro.Cl2.8H2O adding the o.5 Yttria Mixed in the ratio100:16.Citric acid (10g). Processing involved. The mixing of solution, heating, calcinations grinding process. the calcinations of YSZ Powder was confirmed for 3h. The scanning electron microscopic SEM observation is 1μm average particle size .Ph of the complexed solution was adjusted to 8.0 to 8.5 by adding liquor ammonia. After combustion reactions black foam mass was obtained .the crystallizations behavior of powder was analyzed by thermal analysis and XRD techniques. Based on the XRD analysis, the obtained powder was finally calcined at 800 ºC to obtained YSZ powder.
Description: M.Tech.
URI: http://hdl.handle.net/10266/1320
Appears in Collections:Electronic Theses & Dissertations @ TIET

Files in This Item:
File Description SizeFormat 
combine.pdf8 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.